Physical Properties物理性質(zhì) |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Density密度 |
1.40 g/cc |
0.0506 lb/in³ |
DAM; ISO 1183 |
|
Linear Mold Shrinkage, Flow線性收縮率/流動(dòng) |
0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4 |
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向 |
0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4 |
|
Mechanical Properties力學(xué)性能 |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Tensile Strength at Break斷裂拉伸強(qiáng)度 |
200 MPa @Temperature 23.0 °C |
29000 psi @Temperature 73.4 °F |
DAM; ISO 527 |
|
Elongation at Break斷裂伸長(zhǎng)率 |
3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
|
Tensile Modulus拉伸模量 |
11.0 GPa @Temperature 23.0 °C |
1600 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
|
Flexural Modulus彎曲彈性模量 |
10.0 GPa @Temperature 23.0 °C |
1450 ksi @Temperature 73.4 °F |
DAM; ISO 178 |
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度(ISO) |
13.0 kJ/m² @Temperature -40.0 °C |
6.19 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 180/1A |
|
15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
|
|
Charpy ImPAct, Notched夏比缺口沖擊 |
1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
DAM; ISO 179/1eA |
|
1.40 J/cm² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
|
|
Electrical Properties |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Volume ResiSTivity體積電阻率 |
2.00e+18 ohm-cm @Temperature 23.0 °C |
2.00e+18 ohm-cm @Temperature 73.4 °F |
DAM; IEC 60093 |
|
Surface Resistance表面電阻 |
4.00e+15 ohm @Temperature 23.0 °C |
4.00e+15 ohm @Temperature 73.4 °F |
DAM; IEC 60093 |
|
Thermal Properties熱性能 |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Deflection Temperature at熱變形溫度1.8 MPa (264 psi) |
250 °C |
482 °F |
DAM; ISO 75-1/-2 |