Physical Properties物理性質(zhì) |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Density密度 |
1.49 g/cc |
0.0538 lb/in³ |
DAM; ISO 1183 |
|
Filler Content填料含量 |
43 % |
43 % |
DAM |
|
Water Absorption吸水率 |
2.2 % @Thickness 1.00 mm, Temperature 23.0 °C |
2.2 % @Thickness 0.0394 in, Temperature 73.4 °F |
Equilibrium 50%RH; DAM; ISO 62, Similar to |
|
7.6 % @Thickness 1.00 mm, Temperature 23.0 °C |
7.6 % @Thickness 0.0394 in, Temperature 73.4 °F |
Saturation, immersed; DAM; ISO 62, Similar to |
|
|
Linear Mold Shrinkage, Flow線性收縮率/流動(dòng) |
0.0030 cm/cm @Thickness 2.00 mm |
0.0030 in/in @Thickness 0.0787 in |
Parallel; DAM; ISO 294-4 |
|
Linear Mold Shrinkage, Transverse線性收縮率/橫向 |
0.0090 cm/cm @Thickness 2.00 mm |
0.0090 in/in @Thickness 0.0787 in |
Normal; DAM; ISO 294-4 |
|
Mechanical Properties力學(xué)性能 |
Metric公制數(shù)據(jù) |
English英制數(shù)據(jù) |
Comments測(cè)試方法 |
|
Tensile Strength at Break斷裂拉伸強(qiáng)度 |
160 MPa @Temperature 23.0 °C |
23200 psi @Temperature 73.4 °F |
50%RH; ISO 527 |
|
225 MPa @Temperature 23.0 °C |
32600 psi @Temperature 73.4 °F |
DAM; ISO 527 |
|
|
Elongation at Break斷裂伸長(zhǎng)率 |
2.5 % @Temperature 23.0 °C |
2.5 % @Temperature 73.4 °F |
DAM; ISO 527 |
|
3.5 % @Temperature 23.0 °C |
3.5 % @Temperature 73.4 °F |
50%RH; ISO 527 |
|
|
Tensile Modulus拉伸模量 |
11.0 GPa @Temperature 23.0 °C |
1600 ksi @Temperature 73.4 °F |
50%RH; ISO 527 |
|
14.0 GPa @Temperature 23.0 °C |
2030 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
|
|
Izod Impact, Notched懸臂梁缺口沖擊強(qiáng)度 (ISO) |
14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
|
16.0 kJ/m² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 180/1A |
|
|
Charpy Impact Unnotched夏比缺口試樣沖擊 |
9.00 J/cm² @Temperature 23.0 °C |
42.8 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eU |
|
9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
50%RH; ISO 179/1eU |